Control of the properties of electrospun polycaprolactone can be achieved by adjusting the acetic acid:water ratio used to dissolve and electrospin the polymer. In this work, we studied the effect of using up to 15 wt% water in the solvent mixture. Solution conductivity and viscosity and fibre morphology vary dramatically with water content and solution age. Two days after initial solution preparation, electrospinning yields regular fibres for a water content of 0 wt% and 5 wt%, irregular fibres for a 10 wt% water content and irregular and fused fibres for a 15 wt% water content. Fibres with the highest crystallinity (60%) were obtained from solutions containing 5 wt% water while the highest elastic modulus (8.6 ± 1.4 MPa) and tensile stress (4.3 ± 0.3 MPa) pertain to fibres obtained from solutions containing 10 wt% water. Enzymatic fibre degradation is faster the higher the water content in the precursor solution. Adhesion ratio of human foetal fibroblasts was highest on scaffolds obtained from precursor solutions containing 0 wt% water. Cell population increases for all scaffolds and populations quickly become equivalent, with no statistically significant differences between them. Cells exhibit a more extended morphology on the 5 wt% scaffold and a more compact morphology on the 0 wt% scaffold. In summary, a small water content in the solvent allows a significant control over fibre diameter, scaffold properties and the production of scaffolds that support cell adhesion and proliferation. This strategy can be used in soft tissue engineering to influence cell behaviour and the degradation rate of the scaffolds.

Bone grafting and surgical interventions related with orthopaedic disorders consist in a big business, generating large revenues worldwide every year. There is a need to replace the biomaterials that currently still dominate this market, i.e., autografts and allografts, due to their disadvantages, such as limited availability, need for additional surgeries and diseases transmission possibilities. The most promising replacement materials are biomaterials with bioactive properties, such as the calcium phosphate-based bioceramics group. The bioactivity of these materials, i.e., the rate at which they promote the growth and directly bond with the new host biological bone, can be enhanced through their electrical polarization.
In the present work, the electrical polarization features of pure hydroxyapatite (Hap), pure β-tricalcium phosphate (β-TCP) and biphasic hydroxyapatite/β-tricalcium phosphate composites (HTCP) were analyzed by measuring thermally stimulated depolarization currents (TSDC). The samples were thermoelectrically polarized at 500 °C under a DC electric field with a magnitude of 5 kV/cm. The biphasic samples were also polarized under electric fields with different magnitudes: 2, 3, 4 and 5 kV/cm. Additionally, the depolarization processes detected in the TSDC measurements were correlated with dielectric relaxation processes observed in impedance spectroscopy (IS) measurements.
The results indicate that the β-TCP crystalline phase has a considerable higher ability to store electrical charge compared with the Hap phase. This indicates that it has a suitable composition and structure for ionic conduction and establishment of a large electric charge density, providing great potential for orthopaedic applications.

The incorporation of thermosensitive microgels that can act as active sites into polymeric fibers through colloidal electrospinning originates multifunctional, highly porous, and biocompatible membranes suitable for biomedical applications. The use of polyvinylpyrrolidone (PVP), a biocompatible, water-soluble polymer as a fiber template, not only allows the use of a simple set-up to produce composite membranes, but also avoids the use of organic solvents to prepare such systems. Further crosslinking with ultraviolet (UV) radiation avoids membrane dissolution in physiological conditions. Highly porous, UV crosslinked composite membranes with monodisperse mean fiber diameters around 530 nm were successfully produced. These composite membranes showed a Young Modulus of 22 MPa, and an ultimate tensile strength of 3 MPa, accessed in the mechanical tests. Furthermore, the same composite membranes were able to swell about 30 times their weight after 1 hour in aqueous medium. In this work composite multifunctional membranes were designed and extensively studied. PVP, a biocompatible water-soluble polymer, was used as a fiber template to incorporate thermoresponsive poly-(N-isopropylacrylamide) (PNIPAAm)-based microgels into the composite membrane using colloidal electrospinning. The design of multifunctional membranes can be further tailored to several biomedical applications such as temperature-controlled drug delivery systems.

In the present work composite nanoparticles with a magnetic core and a chitosan-based shell were produced as drug delivery systems for doxorubicin (DOX). The results show that composite nanoparticles with a hydrodynamic diameter within the nanometric range are able to encapsulate more DOX than polymeric nanoparticles alone corresponding also to a higher drug release. Moreover the synthesis method of the iron oxide nanoparticles influences the total amount of DOX released and a high content of iron oxide nanoparticles inhibits DOX release. The modelling of the experimental results revealed a release mechanism dominated by Fickian diffusion.

The present work proposes the development of a bio-battery composed by an ultrathin monolithic structure of an electrospun cellulose acetate membrane, over which was deposited metallic thin film electrodes by thermal evaporation on both surfaces. The electrochemical characterization of the bio-batteries was performed under simulated body fluids like sweat and blood plasma [salt solution–0.9% (w/w) NaCl]. Reversible electrochemical reactions were detected through the cellulose acetate structure. Thus, a stable electrochemical behavior was achieved for a bio-battery with silver and aluminum thin films as electrodes. This device exhibits the ability to supply a power density higher than 3 muW cm(-2). Finally, a bio-battery prototype was tested on a sweated skin, demonstrating the potential of applicability of this bio-device as a micropower source.

Iron oxide nanoparticles (NPs) have been extensively studied in the last few decades for several biomedical applications such as magnetic resonance imaging, magnetic drug delivery and hyperthermia. Hyperthermia is a technique used for cancer treatment which consists in inducing a temperature of about 41–45 °C in cancerous cells through magnetic NPs and an external magnetic field. Chemical precipitation was used to produce iron oxide NPs 9 nm in size coated with oleic acid and trisodium citrate. The influence of both stabilizers on the heating ability and in vitro cytotoxicity of the produced iron oxide NPs was assessed. Physicochemical characterization of the samples confirmed that the used surfactants do not change the particles' average size and that the presence of the surfactants has a strong effect on both the magnetic properties and the heating ability. The heating ability of Fe3O4 NPs shows a proportional increase with the increase of iron concentration, although when coated with trisodium citrate or oleic acid the heating ability decreases. Cytotoxicity assays demonstrated that both pristine and trisodium citrate Fe3O4 samples do not reduce cell viability. However, oleic acid Fe3O4 strongly reduces cell viability, more drastically in the SaOs-2 cell line. The produced iron oxide NPs are suitable for cancer hyperthermia treatment and the use of a surfactant brings great advantages concerning the dispersion of NPs, also allowing better control of the hyperthermia temperature.

Chitosan is a biopolymer widely used for biomedical applications such as drug delivery systems, wound healing, and tissue engineering. Chitosan can be used as coating for other types of materials such as iron oxide nanoparticles, improving its biocompatibility while extending its range of applications.
In this work iron oxide nanoparticles (Fe3O4 NPs) produced by chemical precipitation and thermal decomposition and coated with chitosan with different molecular weights were studied. Basic characterization on bare and chitosan-Fe3O4 NPs was performed demonstrating that chitosan does not affect the crystallinity, chemical composition, and superparamagnetic properties of the Fe3O4 NPs, and also the incorporation of Fe3O4 NPs into chitosan nanoparticles increases the later hydrodynamic diameter without compromising its physical and chemical properties. The nano-composite was tested for magnetic hyperthermia by applying an alternating current magnetic field to the samples demonstrating that the heating ability of the Fe3O4 NPs was not significantly affected by chitosan.

The tensile properties of cross-linked and uncross-linked composite films (thickness ∼20–35 μm) prepared from Hydroxypropylcellulose (HPC) with incorporation of microcrystalline cellulose fibers (Avicel) were studied. The concentration of fibers in the composites ranged from 0 to 30 w/w% and cross-linked composites were obtained by the reaction of HPC-Avicel mixtures with 1,4-butyldiisocyanate. It was demonstrated that the inclusion of fibers in a HPC matrix produces composites with enhanced mechanical properties that are improved by cross-linking. Mechanical results seem to indicate that the elastic deformation of the cross-linked composites is predominantly dominated by the fiber content while the cross-linking affects mainly the plastic deformation. Maximum values of the Young's Modulus, yield stress and tensile stress were observed at 10 w/w% for the cross-linked and 20 w/w% for the uncross-linked composites. Furthermore cross-linked films with 10 w/w% of fibers present values of yield stress and tensile stress that are in average 15 to 20% higher than those obtained for uncross-linked composites with 20 w/w% of fibers. Studies in Polarizing Optical Microscopy and Atomic Force Microscopy (AFM) seem to indicate that tensile properties of these composites are correlated to the packing of fibers. For the concentration of the utilized cross-linking agent, and for a fiber content of 10 w/w%, an optimal packing of fibers throughout the matrix has been correlated to the minimal difference between the roughness parameters obtained by AFM analysis of the top and bottom surfaces of the films.

Sub-micrometric Co fibers were prepared via a modified polyol process at 90 °C under an external magnetic field of about 550 Oe, using ethelyne glycol as solvent and hydrazine as reducing agent. The structure, the size and the morphology of the as-elaborated products were highly controlled through properly monitoring the synthesis parameters (amount of NaOH added, the amount of the reducing agent, precursor’ concentration and precursors mixing protocol). The XRD characterization confirmed the formation of pure cobalt powders with either hexagonal compact (hcp) or face-centered-cubic (fcc) structure depending on the concentration of the metal precursor and sodium hydroxide. The scanning electron microscopy observations of the powders shows sub-micrometric fibers with about 0.4–0.6 µm in diameter and a length that could reach 15 µm. Fibers prepared at high reducing ratio were constituted of flower-like spheres that coalesce in the direction of the applied magnetic field. For their high contact surface, these fibers offer new opportunities for catalysis applications. The hysteresis loop measurements show an enhancement of the Hc of the as-obtained fibers compared to their bulk counterparts and permit to confirm the relationship between the structure and the magnetic properties of the materials.

Nanometric and sub-micrometric monodispersed hydroxyapatite (HAp) particles with different morphologies (spheres and rods) were synthesized via a simple solvothermal method using Ca(NO3)2·4H2O and P2O5 as starting materials without any requirement to use organic templates. The growth, evolution and purity of the nanoparticles were investigated by controlling the synthesis conditions, including the alkalinity and the temperature of the solvothermal treatment. The increasing of the alkaline ratio results in a great change of the elaborated particles’ morphology that evolved from anisotropic forms (nanorods, sub-micrometric rod) at pH 9, short rod particles at pH 9.5 to spherical ones at higher pH (pH≥10).
Powder X-Ray diffractometry (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FTIR) and Nitrogen adsorption and desorption studies (BET) were used to characterize the structure and composition of the as-prepared samples.
The thermal analysis of the synthesized particles conducted by differential scanning calorimetry (DSC) shows a good stability for all morphologies with a degradation temperature reaching 1300 °C.

We assembled a new electrospinning apparatus and used poly(ethylene oxide) as a model polymer to perform a systematic study on the influence of solution and processing parameters on the morphology of electrospun nanofibers. Solution parameters studied were polymer concentration and molecular mass. The solvent used, 60 wt% water,40 wt% ethanol, was the same throughout the study. Processing parameters analyzed were: solution feed rate, needle tip-collector distance and electrostatic potential difference between the needle and collector. Solution viscosity increased both with polymer concentration and molecular mass. Polymer concentration plays a decisive role on the outcome of the electrospinning process: a low concentration led to the formation of beaded fibers; an intermediate concentration yielded good quality fibers; a high concentration resulted in a bimodal size distribution and at even higher concentration a distributed deposition. Fiber diameter increased with polymer molecular mass and higher molecular masses are associated with a higher frequency of splaying events. Fiber diameter increased linearly with solution feed rate. While an increase in needle-collector distance represents a weaker electric field, a greater distance to be covered by the fibers and a longer flight time, presumably favoring the formation of thinner fibers, as solvent evaporation leads to a local increase of concentration and viscosity, viscoelastic forces opposing stretching caused an increase of fiber diameter with needle-collector distance. A higher voltage applied at the needle is associated with a higher charging of the polymer and a higher electrical current through it ultimately leading to incomplete solvent evaporation and merged fibers being produced. Controlling the charging of the polymer independently of the electric field strength was achieved by applying a voltage to the collector while distance and potential difference were kept constant. The increased electrostatic repulsion associated with an increase of the high voltage applied to the needle led to the disappearance of merged fibers.

Biodegradable polyurethanes have been studied as scaffolds for tissue engineering due to their adjustable physico-chemical properties. In this work, we synthesized a biodegradable gelatin-based poly(urethane urea) using polycaprolactone-diol, as soft segment, and isophorone diisocyanate and gelatin from cold water fish skin as hard segment. The synthesis was confirmed by Fourier transform infrared spectroscopy and proton nuclear magnetic resonance and the influence of the amount of gelatin introduced in the polymer backbone was analyzed by thermal analysis. Gelatin-based poly(urethane urea) electrospun fibrous mats and solvent cast films were then produced and their physico-chemical and biological properties studied. They present an amorphous structure, elastomeric behavior and water contact angles typical of hydrophobic surfaces. Hydrolytic degradation was analyzed in phosphate buffer saline (PBS), lipase and trypsin solutions. No mass changes were detected during 37 days in PBS and trypsin while significant degradation by lipase was observed. Human foetal foreskin fibroblasts were seeded on the fibrous mats and films. Populations were evaluated by colorimetric cell viability assays and morphology by fluorescence imaging. The substrates supported cell adhesion and proliferation. The novel gelatin-based poly(urethane urea) fibrous mats offer attractive physico-chemical and biological properties for soft tissue engineering applications.

In this work, eco-friendly magnesium-silicide (Mg2Si) semiconducting (n-type) thermoelectric pastes for building components concerning energy-harvesting devices through 3D printing, spray and electrospinning were synthetized and tested for the first time. The Mg2Si fine powders were obtained through the combination of ball milling and thermal annealing under Ar atmosphere. While the latter process was crucial for obtaining the desired Mg2Si phase, the ball milling was indispensable for homogenizing and reducing the grain size of the powders. The synthetized Mg2Si powders exhibited a large Seebeck coefficient of ~ 487 µV/K and were blended with a polymeric solution in different mass ratios to adjust the paste viscosity to the different requirements of 3D printing, electrospinning and low-pressure spray. The materials produced in every single stage of the paste synthesis were characterized by a variety of techniques that unequivocally prove their viability for producing thermoelectric parts and components. These can certainly trigger further research and development in green thermoelectric generators (TEGs) capable of adopting any form or shape with enhanced thermoelectric properties. These green TEGs are meant to compete with common toxic materials such as Bi2Te3, PbTe and CoSb that have Seebeck coefficients in the range of ~ 290–700 μV/K, similar to that of the produced Mg2Si powders and lower than that of 3D printed bulk Mg2Si pieces, measured to be ~ 4866 μV/K. Also, their measured thermal conductivities proved to be significantly lower (~ 0.2 W/mK) than that reported for Mg2Si (≥ 4 W/mK). However, it is herein demonstrated that such thermoelectric properties are not stable over time. Pressureless sintering proved to be indispensable, but difficultly achievable by long thermal annealing (even above 32 h) in inert atmosphere at 400 °C, at least for bulk Mg2Si pieces constituted by a mean grain size of 2–3 μm. Hence, for overcoming this sintering challenge and become the silicide’s extrusion viable in the production of bulk thermoelectric parts, alternative pressureless sintering methods will have to be further explored.

Truncated sialylated O-glycans, such as cell-surface carbohydrate antigen sialyl-Tn (STn) are overexpressed by several cancer types, but not by the respective normal tissues. STn expression is associated with oncogenesis and metastatic ability of cancer cells, with reduced overall survival and lack of response to chemotherapy. Advances in nanomedicine have resulted in rapid development of biocompatible superparamagnetic iron oxide nanoparticles (SPIONs) with considerable potential in cancer treatment. Therefore, in this study SPIONs coated with oleic acid (OA) or dimercaptosuccinic acid (DMSA) were developed and characterized for internalization in two breast cancer cell lines: cell line expressing the STn antigen and the corresponding control. SPIONs with an average diameter of 8 nm showed superparamagnetic behavior and high potential to be used as magnetic hyperthermia agents. OA and DMSA coating provided high stability of SPIONs in physiological conditions while not changing their main properties. NPs internalization studies showed a higher accumulation of DMSA coated NPs in the breast cancer MDA-MB-231 WT cell line. In MDA-MB-231 cell line expressing STn both coated NPs showed a similar accumulation. Therefore, STn antigen can act as a receptor capable of detecting and covalently bind to the molecules present on NPs surface and induce their cellular uptake by endocytosis.

Electrospun fibers of poly[(9,9-dioctylfluorenyl-2,7-diyl)-co-bithiophene] (F8T2) with exceptional electro-optical performance are obtained. The I/T characteristics measured in fibers with 7–15 µm diameter and 1 mm length show a semiconductor behavior; their thermal activation energy is 0.5 eV and the dark conductivity at RT is 5 × 10−9 (Ω cm)−1. Besides exhibiting a photosensitivity of about 60 under white light illumination with a light power intensity of 25 mW · cm−2, the fibers also attain RT photoluminescence in the cyan, yellow, and red wavelength range under ultraviolet, blue, and green light excitation, respectively. Optical microscope images of F8T2 reveal homogeneous electrospun fibers, which are in good agreement with the uniformly radial fluorescence observed.

The thermally stimulated discharge current, the final thermally stimulated discharge current, DC conductivity and the final thermally stimulated discharge current with partially blocking electrode measures were used to analyze electrical behavior of Nylon 11. The objective was to discriminate between dipole related effects and space charge related effects. The space charge effects are dominant in the temperature range from room temperature to 170 °C. By using a Teflon-FEP partially blocking electrode, the space charge injected in the sample is diminished and the effects related to dipole movement can be observed. Beside the two known relaxations for Nylon 11, one associated with the glass transition around 60 °C and a second one associated with a molecular motion in the rigid-amorphous phase at 96 °C, a weak relaxation was observed around 168 °C. The peak around 96 °C is quite broad been composed of two narrow peaks. The final thermally stimulated discharge current method allows a better selection of the experimental conditions for sample charging (polarization) to have only a partial overlap between the nearby peaks. The peak's maximum current and temperature are dependent on the ratio between the charging and discharging time and temperature given a possibility to discriminate between dipolar and space charge effects. A pyroelectric current changes sign around 140 °C indicating that the amidegroup dipoles are frozen in opposite directions when the sample temperature is below 140 °C (amorphous and rigid-amorphous phase) or above (crystalline phase). The conductivity is controlled by the competition between n(E,T) and μ(E,T) indicating a space charge controlled conductivity mechanism.

Hydroxyapatite (HAp) scaffolds with uniform pore size and interconnected pore network were constructed based on the inverted colloidal crystal (ICC) geometry and a simple sol-gel formulation. Monodisperse polystyrene microspheres were self-assembled and annealed into a hexagonal close packed structure. HAp sol-gel was infiltrated in this template followed by thermal treatment for simultaneous HAp matrix sintering and polymeric colloidal crystal calcination. The resultant ICC scaffolds exhibit an ordered architecture that was able to offer a favorable environment for human osteoblasts adhesion and proliferation, an essential feature for bone ingrowth in tissue engineering applications.

Functionalized electrospun fibers are of great interest for biomedical applications such as in the design of drug delivery systems. Nevertheless, in some cases the molecules of interest have poor solubility in water or have high melting temperatures. These drawbacks can be overcome using deep eutectic solvents. In this work, poly(vinyl alcohol) (PVA), a common biodegradable biopolymer, was used to produce new functionalized fibers with the eutectic mixture choline chloride:citric acid in a molar ratio of (1:1) ChCl:CA (1:1), which was used as a model system. Fibers were produced from an aqueous solution with 7.8% (w/v) and 9.8% (w/v) of 95% hydrolyzed PVA and a 2% (v/v) of ChCl:CA (1:1). Smooth, uniform fibers with an average diameter of 0.4 μm were obtained with a content of 19.8 wt % of ChCl:CA (1:1) encapsulated.

Fast-dissolving delivery systems (FDDS) have received increasing attention in the last years. Oral drug delivery is still the preferred route for the administration of pharmaceutical ingredients. Nevertheless, some patients, e.g. children or elderly people, have difficulties in swallowing solid tablets. In this work, gelatin membranes were produced by electrospinning, containing an encapsulated therapeutic deep-eutectic solvent (THEDES) composed by choline chloride/mandelic acid, in a 1:2 molar ratio. A gelatin solution (30% w/v) with 2% (v/v) of THEDES was used to produce electrospun fibers and the experimental parameters were optimized. Due to the high surface area of polymer fibers, this type of construct has wide applicability. With no cytotoxicity effect, and showing a fast-dissolving release profile in PBS, the gelatin fibers with encapsulated THEDES seem to have promising applications in the development of new drug delivery systems.

A novel liquid-crystalline polymer, the toluene-4-sulphonyl urethane of hydroxypropylcellulose (TSUHPC), was prepared through chemical modification of hydroxypropylcellulose (HPC) of Mw = 60000 g mol−1. The resulting polymer was characterized by infrared spectroscopy, differential scanning calorimetry (DSC) and polarizing microscopy. It was found that thermotropic liquid crystal phases are formed between about 60°C and 110°C. Concentrated solutions of TSUHPC in acetone and N,N-dimethylacetamide exhibit cholesteric behaviour, at room temperature. When approaching the lyotropic mesophase to solid transition, either by cooling or by solvent evaporation, very interesting arborescent structures of a seemingly fractal nature may be observed, depending on the kinetics of the transition. A banded texture can be observed when the polymer is sheared near the transition to the isotropic phase.

Peri-implantitis is an infectious disease that affects about one of five patients who receive a dental implant within 5 years after the surgery. To minimize this reaction the development of new biomaterials with antibacterial action is needed that can be used as a coating material in orthodontic implants. In addition, these biomaterials can be doped with several ions, which add specific properties that may act at the cellular level, such as increasing the angiogenesis efficiency. In this work, 45S5 Bioglass® has been used as the base material because it presents higher bioactivity compared to other biomaterials. To add antibacterial function and increase positive effects on bone metabolism, zinc and magnesium ions were introduced in the glass network. The main objective was the synthesis of the 45S5 glass by melt-quenching and study the biological performance as function of the zinc and magnesium concentrations. The structural and biological properties of the prepared samples are discussed.

Scaffolding is at the heart of tissue engineering but the number of techniques available for turning biomaterials into scaffolds displaying the features required for a tissue engineering application is somewhat limited. Inverted colloidal crystals (ICCs) are inverse replicas of an ordered array of monodisperse colloidal particles, which organize themselves in packed long-range crystals. The literature on ICC systems has grown enormously in the past 20 years, driven by the need to find organized macroporous structures. Although replicating the structure of packed colloidal crystals (CCs) into solid structures has produced a wide range of advanced materials (e.g., photonic crystals, catalysts, and membranes) only in recent years have ICCs been evaluated as devices for medical/pharmaceutical and tissue engineering applications. The geometry, size, pore density, and interconnectivity are features of the scaffold that strongly affect the cell environment with consequences on cell adhesion, proliferation, and differentiation. ICC scaffolds are highly geometrically ordered structures with increased porosity and connectivity, which enhances oxygen and nutrient diffusion, providing optimum cellular development. In comparison to other types of scaffolds, ICCs have three major unique features: the isotropic three-dimensional environment, comprising highly uniform and size-controllable pores, and the presence of windows connecting adjacent pores. Thus far, this is the only technique that guarantees these features with a long-range order, between a few nanometers and thousands of micrometers. In this review, we present the current development status of ICC scaffolds for tissue engineering applications.

High-entropy alloys (HEAs) have been around since 2004. The breakthroughs in this field led to several potential applications of these alloys as refractory, structural, functional, and biomedical materials. In this work, a short overview on the concept of high-entropy alloys is provided, as well as the theoretical design approach. The special focus of this review concerns one novel class of these alloys: biomedical high-entropy alloys. Here, a literature review on the potential high-entropy alloys for biomedical applications is presented. The characteristics that are required for these alloys to be used in biomedical-oriented applications, namely their mechanical and biocompatibility properties, are discussed and compared to commercially available Ti6Al4V. Different processing routes are also discussed.

The incorporation of magnetic nanoparticles into poly(N-isopropylacrylamide) (PNIPAAm) and chitosan microgels gives rise to hybrid systems that combine the microgels swelling capacity with the interesting features presented in magnetic nanoparticles. The presence of chitosan that act as surfactant for magnetic nanoparticles provides a simplistic approach which allows the encapsulation of magnetic nanoparticles without any previous surface modification. Spherical and highly monodisperse microgels with diameters in the range of 200 to 500 nm were obtained. The encapsulation of magnetic nanoparticles in the polymer matrix was confirmed by high resolution Scanning Electron Microscopy in transmission mode. Volume phase transition of the microgels was accessed by Dynamic Light Scattering measurements. It was observed that the thermosensitivity of the PNIPAM microgels still persists in the hybrid microgels; however, the swelling ability is compromised in the microgels with highest chitosan content. The heating performance of the hybrid magnetic microgels, when submitted to an alternating magnetic field, was also evaluated demonstrating the potential of these systems for hyperthermia treatments.

Bacterial infections affect about 1 in 5 patients who receive a dental implant within 5 years of surgery. To avoid the implant rejection it is necessary for the development of innovative biomaterials, with addition or substitution of the ions, for implant coatings that promote a strong bond with the new host bone and antibacterial action. The objective of this work was to synthesize a bioactive glass with different silver concentrations to evaluate their antibacterial performance. The glasses were synthesized with up to 2% silver content by melt-quenching. Structural, morphological, biological, and electrical properties of all samples were studied. The biological behavior was evaluated through cytotoxicity tests and antibacterial activity. The structural analysis shows that the introduction of silver do not promote significant changes, not altering the advantageous properties of the bioglass of the bioglass. It was verified that the glasses with a silver content from 0.5% to 2%, completely prevented the growth of both Staphylococcus aureus and Escherichia coli while being nontoxic toward mammalian cells. Therefore, these bioglasses are promising materials to be used in the production of dental implants with antimicrobial activity.

Several problems and limitations faced in the treatment of many diseases can be overcome by using controlled drug delivery systems (DDS), where the active compound is transported to the target site, minimizing undesirable side effects. In situ-forming hydrogels that can be injected as viscous liquids and jellify under physiological conditions and biocompatible clay nanoparticles have been used in DDS development. In this work, polymer–clay composites based on Pluronics (F127 and F68) and nanoclays were developed, aiming at a biocompatible and injectable system for long-term controlled delivery of methylene blue (MB) as a model drug. MB release from the systems produced was carried out at 37 °C in a pH 7.4 medium. The Pluronic formulation selected (F127/F68 18/2 wt.%) displayed a sol/gel transition at approx. 30 °C, needing a 2.5 N force to be injected at 25 °C. The addition of 2 wt.% of Na116 clay decreased the sol/gel transition to 28 °C and significantly enhanced its viscoelastic modulus. The most suitable DDS for long-term application was the Na116-MB hybrid from which, after 15 days, only 3% of the encapsulated MB was released. The system developed in this work proved to be injectable, with a long-term drug delivery profile up to 45 days.

The present work deals with the preparation and the characterisation of solid films, having thickness between 15 and 40 μm, prepared with hydroxypropyl cellulose (HPC) and different amounts of commercial cellulose fibres (0; 0.5; 10 and 15% w/w) (system A) and with 1,4-butyl diisocyanate (BDI), as a cross-linking agent (system B). Before the preparation of these films, the surface energy of cellulose fibres, as such and after purification with different solvents, was determined by Inverse Gas Chromatography (IGC), which gave the values of dispersive energy and acid-base properties of their surfaces. The tensile and photo-elastic properties of the solid films obtained were studied. There were no significant changes in Young's modulus between the two systems. However, as expected, the values of the elongation and those of the fracture stress were systematically higher for system B in comparison with system A. The same trend was found for the birefringence, measured at the same elongation values for the films obtained from both systems.

Cellulose and chitin are the two most abundant natural polysaccharides. Both have a semicrystalline microfibrillar structure from which nanofibres can be extracted. These nanofibres are rod-like microcrystals that can be used as nanoscale reinforcements in composites due to their outstanding mechanical properties. This chapter starts by reviewing the sources, extraction methods and properties of cellulose and chitin nanofibres. Then, their use in the fabrication of structural and functional nanocomposites and the applications that have been investigated are reviewed. Nanocomposites are materials with internal nano-sized structures. They benefit from the properties of the nanofillers: low density, nonabrasive, nontoxic, low cost, susceptibility to chemical modifications and biodegradability. Diverse manufacturing technologies have been used to produce films, fibres, foams, sponges, aerogels, etc. Given their natural origin and high stiffness, these polymers have attracted a lot of attention not only in the biomedical and tissue engineering fields but also in areas such as pharmaceutics, cosmetics, agriculture, biosensors and water treatment.

The physical properties of the cubic and ferrimagnetic spinel ferrite LiFe5O8 has made it an attractive material for electronic and medical applications. In this work, LiFe5O8 nanosized crystallites were synthesized by a novel and eco-friendly sol-gel process, by using powder coconut water as a mediated reaction medium. The dried powders were heat-treated (HT) at temperatures between 400 and 1000 °C, and their structure, morphology, electrical and magnetic characteristics, cytotoxicity, and magnetic hyperthermia assays were performed. The heat treatment of the LiFe5O8 powder tunes the crystallite sizes between 50 nm and 200 nm. When increasing the temperature of the HT, secondary phases start to form. The dielectric analysis revealed, at 300 K and 10 kHz, an increase of ε′ (≈10 up to ≈14) with a tanδ almost constant (≈0.3) with the increase of the HT temperature. The cytotoxicity results reveal, for concentrations below 2.5 mg/mL, that all samples have a non-cytotoxicity property. The sample heat-treated at 1000 °C, which revealed hysteresis and magnetic saturation of 73 emu g−1 at 300 K, showed a heating profile adequate for magnetic hyperthermia applications, showing the potential for biomedical applications.

Cancer remains as one of the major causes of mortality worldwide. Recent advances in nanoparticles based therapy mark a new era on cancer treatment. Many groups have investigated biological/physical effects of nanoparticles on tumour cells and how these vary with physical parameters such as particle size, shape, concentration and distribution. Magnetic hyperthermia (MHT) can be an alternative or an add-value therapy with demonstrated effectiveness. MHT uses magnetic nanoparticles, which can be directly applied to the tumour, where, by applying an external ac magnetic field, will promote a localized temperature increment that can be controlled.

The objective of this work was to prepare polysaccharide-based gels exhibiting liquid crystalline properties. Such systems may be used in some optical or in biomedical applications, where biodegradability is required. Chitosan is a derivative of chitin, widely used in a series of medical applications. Due to its rigid structure, chitosan or its derivatives may show lyotropic mesophases in certain conditions. In this work, chitosan solutions were prepared by mixing completely the polysaccharide with different concentration of formic, acetic and monochloroacetic acids at room temperature. X-ray diffraction patterns of the gels did not show the existence of a crystalline structure. Finger-prints texture observed by polarised optical microscopy was attributed to a cholesteric liquid crystalline phase that usually develops in concentrated solutions. Values of the nematic chiral pitch (P) were determined in function of acid solution concentration. The critical concentrations (C*) to form a lyotropic liquid crystalline phase in formic, acetic and monochloroacetic acids were determined, and the obtained values were confronted with the expected critical concentration based on the Flory formalism. The critical concentration values were found to be dependent upon the acid used.

Iron oxide nanoparticles (Fe3O4, IONPs) are promising candidates for several biomedical applications such as magnetic hyperthermia and as contrast agents for magnetic resonance imaging (MRI). However, their colloidal stability in physiological conditions hinders their application requiring the use of biocompatible surfactant agents. The present investigation focuses on obtaining highly stable IONPs, stabilized by the presence of an oleic acid bilayer. Critical aspects such as oleic acid concentration and pH were optimized to ensure maximum stability. NPs composed of an iron oxide core with an average diameter of 9 nm measured using transmission electron microscopy (TEM) form agglomerates with an hydrodynamic diameter of around 170 nm when dispersed in water in the presence of an oleic acid bilayer, remaining stable (zeta potential of −120 mV). Magnetic hyperthermia and the relaxivities measurements show high efficiency at neutral pH which enables their use for both magnetic hyperthermia and MRI.

The present paper regards the preparation and characterization of Pluronic F127 + F68/water/poly (ε-caprolactone) microcapsules (MCs) composite systems for tissue repair. The first part of the work relates to the production of poly(ε-caprolactone) (PCL) MCs via water-in-oil-in-water (W/O/W) double emulsion system combined with solvent evaporation method. The study of different process parameters in the final MCs characteristics and their drug release profile is herein reported. Different percentages of PCL, emulsion stabilizer, and volume proportions of the emulsion constituents have been tested, leading to considerable differences in the MCs size distributions. The selected MCs, containing an aqueous solution of methylene blue (MB) as a model drug, were then used to fill a Pluronic F127 + F68/water system leading to the final composite system (5 and 10 wt % MB loaded PCL MCs). The composite systems were characterised in the second part of the work in terms of its rheological behaviour and drug release performance. They were found to gellify at 30 °C, and present an extended drug release to a total of 18 days. The models that best define the release profiles were also studied, with the release of MB occurring mostly by Fick diffusion and polymer chain relaxation. Pluronic F127 + F68/water/poly (ε-caprolactone) MCs composite system is shown to be a promising injectable system, with two different drug release rates, for tissue repair.

In this paper the rheological characterization of Pluronic/water systems filled with alginate microparticles is presented. The rheological characterization of the Pluronic/water systems allowed for the choice of the best Pluronic concentration taking into account its applications as injectable hydrogels for tissue repair. The effect on the rheological behavior of the addition of alginate microparticles, to be loaded with the drug, was analyzed and the maximum concentration of microparticles determined.

A (model) composite system for drug delivery was developed based on a thermoresponsive hydrogel loaded with microparticles. We used Pluronic F127 hydrogel as the continuous phase and alginate microparticles as the dispersed phase of this composite system. It is well known that Pluronic F127 forms a gel when added to water in an appropriate concentration and in a certain temperature range. Pluronic F127 hydrogel may be loaded with drug and injected, in its sol state, to act as a drug delivery system in physiological environment. A rheological characterization allowed the most appropriate concentration of Pluronic F127 (15.5 wt%) and appropriate alginate microparticles contents (5 and 10 wt%) to be determined. Methylene blue (MB) was used as model drug to perform drug release studies in MB loaded Pluronic hydrogel and in MB loaded alginate microparticles/Pluronic hydrogel composite system. The latter showed a significantly slower MB release than the former (10 times), suggesting its potential in the development of dual cargo release systems either for drug delivery or tissue engineering.

Engineering drug delivery systems (DDS) aim to release bioactive cargo to a specific site within the human body safely and efficiently. Hydrogels have been used as delivery matrices in different studies due to their biocompatibility, biodegradability, and versatility in biomedical purposes. Microparticles have also been used as drug delivery systems for similar reasons. The combination of microparticles and hydrogels in a composite system has been the topic of many research works. These composite systems can be injected in loco as DDS. The hydrogel will serve as a barrier to protect the particles and retard the release of any bioactive cargo within the particles. Additionally, these systems allow different release profiles, where different loads can be released sequentially, thus allowing a synergistic treatment. The reported advantages from several studies of these systems can be of great use in biomedicine for the development of more effective DDS. This review will focus on in situ injectable microparticles in hydrogel composite DDS for biomedical purposes, where a compilation of different studies will be analysed and reported herein.

The delivery of multiple anti-cancer agents holds great promise for better treatments. The present work focuses on developing multifunctional materials for simultaneous and local combinatory treatment: Chemotherapy and hyperthermia. We first produced hybrid microgels (MG), synthesized by surfactant-free emulsion polymerization, consisting of Poly (N-isopropyl acrylamide) (PNIPAAm), chitosan (40 wt.%), and iron oxide nanoparticles (NPs) (5 wt.%) as the inorganic component. PNIPAAm MGs with a hydrodynamic diameter of about 1 μm (in their swollen state) were successfully synthesized. With the incorporation of chitosan and NPs in PNIPAAm MG, a decrease in MG diameter and swelling capacity was observed, without affecting their thermosensitivity. We then sought to produce biocompatible and mechanically robust membranes containing these dual-responsive MG. To achieve this, MG were incorporated in poly (vinyl pyrrolidone) (PVP) fibers through colloidal electrospinning. The presence of NPs in MG decreases the membrane swelling ratio from 10 to values between 6 and 7, and increases the material stiffness, raising its Young modulus from 20 to 35 MPa. Furthermore, magnetic hyperthermia assay shows that PVP-MG-NP composites perform better than any other formulation, with a temperature variation of about 1 °C. The present work demonstrates the potential of using multifunctional colloidal membranes for magnetic hyperthermia and may in the future be used as an alternative treatment for cancer.

Hybrid materials have been widely studied for structural applications. Polysaccharide-based fibers, especially cellulosic fibers, have been explored in the last two decades as substitutes of the traditional reinforcements made of glass or carbon fibers due to their mechanical properties. However, their biocompatibility, biodegradability, and chemistry have attracted the researchers and new developments in the field of smart and functional materials arise in diverse applications. This chapter will focus on the biomedical applications of polysaccharide-based smart and functional materials, namely those concerning biosensors and actuators, theranostic systems, and tissue-engineering applications. Special attention will be given to cellulose- and chitin/chitosan-based hybrid materials because these are the two most abundant polysaccharides and probably the most promising for the development of hybrid materials for biomedical applications. Biomimetic strategies for the development of smart and functional hybrid materials will also be highlighted.

We show that suspended nano and microfibres electrospun from liquid crystalline cellulosic solutions will curl into spirals if they are supported at just one end, or, if they are supported at both ends, will twist into a helix of one handedness over half of its length and of the opposite handedness over the other half, the two halves being connected by a short straight section. This latter phenomenon, known as perversion, is a consequence of the intrinsic curvature of the fibres and of a topological conservation law. Furthermore, agreement between theory and experiment can only be achieved if account is taken of the intrinsic torsion of the fibres. Precisely the same behaviour is known to be exhibited by the tendrils of climbing plants such as Passiflora edulis, albeit on a lengthscale of millimetres, i.e., three to four orders of magnitude larger than in our fibres. This suggests that the same basic, coarse-grained physical model is applicable across a range of lengthscales.