Figueira, J., J. Loureiro, J. Marques, C. Bianchi, P. Duarte, M. Ruoho, I. Tittonen, and I. Ferreira, "Optimization of Cuprous Oxides Thin Films to be used as Thermoelectric Touch Detectors", ACS Appl Mater Interfaces, vol. 9, issue 7, pp. 6520-6529, 2017. AbstractDOI

The electronic and optical properties of p-type copper oxides (CO) strongly depend on the production technique as it influences the obtained phases: cuprous oxide (Cu2O) or cupric oxide (CuO), the most common ones. Cu films deposited by thermal evaporation have been annealed in air atmosphere, with temperature between 225 and 375 °C and time between 1 and 4 h. The resultant CO films have been studied to understand the influence of processing parameters in the thermoelectric, electrical, optical, morphological, and structural properties. Films with a Cu2O single phase are formed when annealing at 225 °C, while CuO single phase films can be obtained at 375 °C. In between, both phases are obtained in proportions that depend on the film thickness and annealing time. The positive sign of the Seebeck coefficient (S), measured at room temperature (RT), confirms the p-type behavior of both oxides, showing values up to 1.2 mV·°C–1and conductivity up to 2.9 (Ω·m)−1. A simple detector using Cu2O have been fabricated and tested with fast finger touch events

Sousa, D. M., J. C. Lima, and I. Ferreira, "Synthesis of Cadmium Selenide Quantum Dots, Using 2, 2‐Bipyridine as a Capping and Phase Transfer Agent", ChemistrySelect, vol. 2, issue 3, pp. 1271-1274, 2017. AbstractDOI

Cadmium selenide quantum dots (CdSe QDs), were synthesized by one‐pot or water‐to‐organic phase transfer and capped with molten 2,2′‐bipyridine (bipy). The obtained CdSe QDs by the two‐step procedure, reveal average sizes of 2 nm while the one‐pot are mixed with secondary salt products and bipy and are undetectable by TEM. However the absorption peak of both CdSe QDs was at 425 nm and the emission band is centered at 535 nm, with a band width at half height of 77 nm, when excited with 425 nm light. The two‐step CdSe QDs synthesis has the great advantage of capping the CdSe QDs with bipy, forming a solid phase, which is easily stored and dispersed in most of the organic solvents. On the other hand, the one‐pot procedure requires an extra step to remove the secondary products.

2016
Bari, M., J. Loureiro, M. Pudas, K. Tappura, K. Jaakola, M. Ruoho, I. Tittonen, S. Volz, C. Pavan, K. Costabello, D. Bollen, M. Haslam, and I. Ferreira, "TransFlexTeg: Large area transparent thin film thermoelectric devices for smart window and flexible applications", 14th European Conference on Thermoelectrics, ECT 2016, 20-23 Sep, 2016. Abstract

The main objective of TransFlexTeg is to develop an innovative large area distributed sensor network integrating transparent thin film thermoelectric devices and sensors for multifunctional smart windows and flexible high impact volume applications. Different breakthrough concepts will be developed: 1) large area high performance transparent thermoelectric thin films deposited on flexible substrates for thermal energy harvesting; 2) low cost high throughput thin film thermal sensors for thermal mapping and gesture sensing; 3) flexible smart windows and walls with energy harvesting, environmental sensing and wireless communication functionalities. This technology aims to demonstrate the functionalities of a smart window able to measure air quality and environmental parameters such as temperature, sun radiation and humidity. The data is automatically collected and can be utilized for controlling heating, cooling and ventilation systems of indoors. Active radio interface enables long range communication and long term data collection with WiFi or a similar base station. The proposed concept of smart windows replaces several conventional sensors with a distributed sensor network that is integrated invisibly into windows. In addition to the power generated from the thermal energy harvesting, the thermoelectric elements (TE) are also used as temperature sensors that, while being distributed over large area, enable thermal mapping of the area instead of just one or a few values measured from particular points. This smart window can be produced on glass. The active layer itself can be flexible glass layer or polymer sheet, which will significantly broaden the field of applications and improve business opportunities. Both can be manufactured in batch, or in Roll to Roll Atomic Layer Deposition (R2R ALD) process. High environmental impact is expected with savings of more than 25% of the electrical usage of residential homes and office buildings.

Soares, P. I. P., A. I. Sousa, J. C. Silva, I. M. M. Ferreira, C. M. M. Novo, and J. P. Borges, "Chitosan-based nanoparticles as drug delivery systems for doxorubicin: Optimization and modelling", Carbohydr Polym, vol. 147, pp. 304-312, 2016. AbstractDOI

In the present work, two drug delivery systems were produced by encapsulating doxorubicin into chitosan and O-HTCC (ammonium-quaternary derivative of chitosan) nanoparticles. The results show that doxorubicin release is independent of the molecular weight and is higher at acidic pH (4.5) than at physiological pH. NPs with an average hydrodynamic diameter bellow 200 nm are able to encapsulate up to 70% and 50% of doxorubicin in the case of chitosan and O-HTCC nanoparticles, respectively. O-HTCC nanoparticles led to a higher amount of doxorubicin released than chitosan nanoparticles, for the same experimental conditions, although the release mechanism was not altered. A burst effect occurs within the first hours of release, reaching a plateau after 24 h. Fitting mathematical models to the experimental data led to a concordant release mechanism between most samples, indicating an anomalous or mixed release, which is in agreement with the swelling behavior of chitosan described in the literature.

Mendes, M. J., A. Araújo, A. Vicente, H. Águas, I. Ferreira, E. Fortunato, and R. Martins, "Design of optimized wave-optical spheroidal nanostructures for photonic-enhanced solar cells", Nano Energy, vol. 26, pp. 286-296, 2016. AbstractDOI

The interaction of light with wavelength-sized photonic nanostructures is highly promising for light management applied to thin-film photovoltaics. Several light trapping effects come into play in the wave optics regime of such structures that crucially depend on the parameters of the photonic and absorbing elements. Thus, multi-parameter optimizations employing exact numerical models, as performed in this work, are essential to determine the maximum photocurrent enhancement that can be produced in solar cells.

Generalized spheroidal geometries and high-index dielectric materials are considered here to model the design of the optical elements providing broadband absorption enhancement in planar silicon solar cells. The physical mechanisms responsible for such enhancement are schematized in a spectral diagram, providing a deeper understanding of the advantageous characteristics of the optimized geometries. The best structures, composed of TiO2 half-spheroids patterned on the cells' top surface, yield two times higher photocurrent (up to 32.5 mA/cm2 in 1.5 µm thick silicon layer) than the same devices without photonic schemes.

These results set the state-of-the-art closer to the theoretical Lambertian limit. In addition, the considered light trapping designs are not affected by the traditional compromise between absorption enhancement versus current degradation by recombination, which is a key technological advantage.

João, C. F. C., A. C. Baptista, I. M. M. Ferreira, J. C. Silva, and J. P. Borges, "https://vtt.pure.elsevier.com/en/publications/transflexteg-large-area-transparent-thin-film-thermoelectric-devi", Fibrous and textile materials for composite applications, Singapore, Springer, pp. 261-299, 2016. Abstract

Cellulose and chitin are the two most abundant natural polysaccharides. Both have a semicrystalline microfibrillar structure from which nanofibres can be extracted. These nanofibres are rod-like microcrystals that can be used as nanoscale reinforcements in composites due to their outstanding mechanical properties. This chapter starts by reviewing the sources, extraction methods and properties of cellulose and chitin nanofibres. Then, their use in the fabrication of structural and functional nanocomposites and the applications that have been investigated are reviewed. Nanocomposites are materials with internal nano-sized structures. They benefit from the properties of the nanofillers: low density, nonabrasive, nontoxic, low cost, susceptibility to chemical modifications and biodegradability. Diverse manufacturing technologies have been used to produce films, fibres, foams, sponges, aerogels, etc. Given their natural origin and high stiffness, these polymers have attracted a lot of attention not only in the biomedical and tissue engineering fields but also in areas such as pharmaceutics, cosmetics, agriculture, biosensors and water treatment.

Soares, P. I. P., C. A. T. Laia, A. Carvalho, L. C. J. Pereira, J. T. Coutinho, I. M. M. Ferreira, C. M. M. Novo, and J. P. Borges, "Iron oxide nanoparticles stabilized with a bilayer of oleic acid for magnetic hyperthermia and MRI applications", Appl Surf Sci, vol. 383, pp. 240-247, 2016. AbstractDOI

Iron oxide nanoparticles (Fe3O4, IONPs) are promising candidates for several biomedical applications such as magnetic hyperthermia and as contrast agents for magnetic resonance imaging (MRI). However, their colloidal stability in physiological conditions hinders their application requiring the use of biocompatible surfactant agents. The present investigation focuses on obtaining highly stable IONPs, stabilized by the presence of an oleic acid bilayer. Critical aspects such as oleic acid concentration and pH were optimized to ensure maximum stability. NPs composed of an iron oxide core with an average diameter of 9 nm measured using transmission electron microscopy (TEM) form agglomerates with an hydrodynamic diameter of around 170 nm when dispersed in water in the presence of an oleic acid bilayer, remaining stable (zeta potential of −120 mV). Magnetic hyperthermia and the relaxivities measurements show high efficiency at neutral pH which enables their use for both magnetic hyperthermia and MRI.

Soares, P. I. P., D. Machado, C. Laia, L. C. J. Pereira, J. T. Coutinho, I. M. M. Ferreira, C. M. M. Novo, and J. P. Borges, "Thermal and magnetic properties of chitosan-iron oxide nanoparticles", Carbohydr Polym, vol. 149, pp. 382-390, 2016. AbstractDOI

Chitosan is a biopolymer widely used for biomedical applications such as drug delivery systems, wound healing, and tissue engineering. Chitosan can be used as coating for other types of materials such as iron oxide nanoparticles, improving its biocompatibility while extending its range of applications.

In this work iron oxide nanoparticles (Fe3O4 NPs) produced by chemical precipitation and thermal decomposition and coated with chitosan with different molecular weights were studied. Basic characterization on bare and chitosan-Fe3O4 NPs was performed demonstrating that chitosan does not affect the crystallinity, chemical composition, and superparamagnetic properties of the Fe3O4 NPs, and also the incorporation of Fe3O4 NPs into chitosan nanoparticles increases the later hydrodynamic diameter without compromising its physical and chemical properties. The nano-composite was tested for magnetic hyperthermia by applying an alternating current magnetic field to the samples demonstrating that the heating ability of the Fe3O4 NPs was not significantly affected by chitosan.

Soares, P. I. P., A. I. Sousa, I. M. M. Ferreira, C. M. M. Novo, and J. P. Borges, "Towards the development of multifunctional chitosan-based iron oxide nanoparticles: Optimization and modelling of doxorubicin release", Carbohydr Polym, vol. 153, pp. 212-221, 2016. AbstractDOI

In the present work composite nanoparticles with a magnetic core and a chitosan-based shell were produced as drug delivery systems for doxorubicin (DOX). The results show that composite nanoparticles with a hydrodynamic diameter within the nanometric range are able to encapsulate more DOX than polymeric nanoparticles alone corresponding also to a higher drug release. Moreover the synthesis method of the iron oxide nanoparticles influences the total amount of DOX released and a high content of iron oxide nanoparticles inhibits DOX release. The modelling of the experimental results revealed a release mechanism dominated by Fickian diffusion.

Bianchi, C., J. Loureiro, P. Duarte, J. Marques, J. Figueira, I. Ropio, and I. Ferreira, "V2O5 Thin Films for Flexible and High Sensitivity Transparent Temperature Sensor", Advanced Materials Technologies, vol. 1, issue 6, pp. 1600077, 2016. AbstractDOI

This work reports the optimization of V2O5 Seebeck coefficient to obtain high sensitivity and transparent temperature sensors. It is observed that the film thickness plays a major role on the thermoelectric properties, together with the annealing step, obtaining a Seebeck coefficient of −690 μV K−1, for 75 nm thick V2O5 films deposited on glass, after an annealing step of 1 h at 773 K, in air. The V2O5 films are also deposited and optimized on polyimide substrates, but lower annealing temperature is required, 573 K for 3 h, to maintain the flexibility of the substrate and simultaneously high Seebeck coefficient, −591 μV K−1. These films are used in a simple design sensor and tested on the surface of a microfluidic channel (500 μm) made of polydimethylsiloxane, while having hot water flowing through it. The response time is below 1 s and the recovery time around 5 s.