Silver (Ag) and tin (Sn) nanoparticles (NPs) were deposited by thermal evaporation onto heated glass substrates with a good control of size, shape and surface coverage. This process has the advantage of allowing the fabrication of thin-film solar cells with incorporated NPs without vacuum break, since it does not require chemical processes or post-deposition annealing. The X-ray diffraction, TEM and SEM properties are correlated with optical measurements and amorphous silicon hydrogenated (a-Si:H) films deposited on top of both types of NPs show enhanced absorbance in the near-infrared. The results are interpreted with electromagnetic modelling performed with Mie theory. A broad emission in the near-infrared region is considerably increased after covering the Ag nanoparticles with an a-Si:H layer. Such effect may be of interest for possible down-conversion mechanisms in novel photovoltaic devices.

Emulsion detonation synthesis method was used to produce undoped and Al-doped ZnO nanostructured powders (0.5–2.0 wt.% Al2O3). The synthesized powders present a controlled composition and a morphology which is independent on the doping level. The XRD results indicate wurtzite as the single phase for undoped ZnO and the presence of gahnite as secondary phase for Al-doped ZnO powders. The sintering behavior of each powder was studied based on their linear shrinkage and shrinkage rate curves, showing the high sinterability of the powders. Activation energies for densification in the earlier stage were calculated for all compositions and possible sintering mechanisms are suggested depending on the doping level. The high chemical homogeneity and sinterability and the lower electrical resistivity of the bulk Al-doped sintered samples demonstrates the feasibility of emulsion detonation synthesis for the production of high quality Al-doped ZnO powders to be used in ceramic sputtering targets manufacture.

Cancer is one of the main causes of death in the world and its incidence increases every
day. Current treatments are insufficient and present many breaches. Hyperthermia is an old
concept and was early established as a cancer treatment option, mainly in superficial
cancers. More recently, the concept of intracellular hyperthermia emerged wherein magnetic
particles are concentrated at the tumor site and remotely heated using an applied magnetic
field to achieve hyperthermic temperatures (42-45ºC). Many patents have been registered in
this area since the year 2000. This chapter presents the most relevant information organized
in two main categories according to the use or not of nanotechnology.