Adsorption of model systems of triclosan by mineral sorbent diatomite is studied. The triclosan equilibrium concentration was measured spectrophotometrically, the morphology of the diatomite characterized using scanning electron microscopy and the amount of the adsorbed triclosan on the diatomite quantified by a mass balance. Adsorption isotherms were analyzed according to the linear/nonlinear form of Langmuir, Freundlich, Sips and Toth isotherm models isotherms, using AMPL software. It is shown that nonlinear Langmuir and Sips isotherm model provided suitable fitting results and no pronounced difference in adsorption efficiency between isotherms measured after 1, 2 and 3days adsorption was observed. Determined maximum adsorption capacity of diatomite towards triclosan qs is 140mg/g. Averaged calculated values of ΔG are −9.9 and −9.6kJ/mol for Langmuir and Sips models respectively. The negative sign of such values indicates spontaneous, physical in nature adsorption.

Alkoxylation of α−pinene, β−pinene and limonene was performed in the presence of SBA-15-occluded tungstophosphoric acid (HPW). The HPW was immobilised in SBA-15 using the sol-gel method. The catalysts were characterised by N2 adsorption, FT-IR, Raman spectroscopy, X-Ray diffraction, ICP-AES and TEM. A series of catalysts with different heteropolyacid loadings ranging from 1.8 to 19.3 wt. % were prepared. PW4-SBA-15 (with 10.8 wt. %) exhibited the highest catalytic activity for the alkoxylation of α-pinene with ethanol. An approximately 53% selectivity to α-terpinyl ethyl ether was observed over the PW-SBA-15 catalysts. PW4-SBA-15 was also used as a catalyst for the alkoxylation of other terpenes, including β-pinene and limonene. The PW4-SBA-15 catalyst exhibited high catalytic stability for the alkoxylation of α-pinene with ethanol. PW4-SBA-15 was also used as a catalyst for the esterification of free fatty acids (i.e., palmitic, stearic and oleic acids) with ethanol. Good catalytic activity was observed for the PW4-SBA-15 catalyst with the different substrates used in the esterifications.

The adsorption of triclosan as model system was studied to qualify activated carbon sorbents recycled from gas masks (civilian gas mask GP5). The triclosan equilibrium concentration was measured spectrophotometrically, the morphology of the activated carbon characterized by scanning electron microscopy, and the amount of the adsorbed triclosan on the activated carbon quantified by a mass balance method. Experimental isotherms were fitted by Langmuir, Freundlich and Sips adsorption models. It was obtained that the contact time is a crucial sorption parameter that provides information on the optimum adsorption efficiency. It was shown that the maximum efficiency of GP5 (88%) is obtained after 10days of adsorption at a maximal concentration of triclosan and carbon loading 1mg/l. No significant adsorption efficiency differences were measured after 5 and 10days of adsorption. The non-linear Sips isotherm, a combined Freundlich–Langmuir model, provides suitable fitting results. The observed remarkable adsorption capacity of activated carbon (GP5) towards triclosan adsorption (∼85mg/g) makes it a viable solution for wastewater treatment.