Polymeric parts produced by Fused Deposition Modelling (FDM) Additive Manufacturing (AM) has no special safety requirements, and therefore, NDT is not required. However, the use of AM to produce Fibre Reinforcement Thermoplastics (FRTP) parts means that structural applications with safety requirements are envisaged, demanding reliable NDT methods. This paper presents experimental results and numerical simulation by Finite Element Method (FEM) of the NDT inspection of different parts of polymeric and RFTP composite materials. The parts were produced by FDM Additive Manufacturing and different delamination defects were introduced at different positions and with different dimensions and morphologies. Two different NDT techniques were used, exploiting different inspection parameters: air-coupled ultrasound, using frequencies between 50 and 400 kHz and active transient thermography, in both reflection and transition modes. The influence of the curvature of the parts was analysed, from the experimental point of view, and the results were compared with different numerical simulation strategies. It was shown that, both NDT techniques can detect the defects, with good spatial resolution, being the thermography reflection mode the fastest and expedite for curvature parts. The numerical simulation corroborates the experimental results allowing a deeper insight on the physical phenomena involved.

The present work addressed the challenges of identifying applicable Non-Destructive Testing (NDT) techniques suitable for inspection and materials characterization techniques for Wire and Arc Additive Manufacturing (WAAM) parts. With the view of transferring WAAM to the industry and qualifying the manufacturing process for applications such as structural components, the quality of the produced parts needs to be assured. Thus, the main objective of this paper is to review the main NDT techniques and assess the capability of detecting WAAM defects, for inspection either in a monitoring, in-process or post-process scenario. Radiography and ultrasonic testing were experimentally tested on reference specimens in order to compare the techniques capabilities. Metallographic, hardness and electrical conductivity analysis were also applied to the same specimens for material characterization. Experimental outcomes prove that typical WAAM defects can be detected by the referred techniques. The electrical conductivity measurement may complement or substitute some destructive methods used in AM processing.