Online monitoring of carbon fibre reinforced polymer (CFRP) components requires a Non-Destructive Testing (NDT) method capable of contactless sensing of damage, while enabling high inspection speeds needed for monitoring large components. Eddy current testing (ECT) of CFRP components has great potential for two reasons. First, ECT probes are capable of operating without contact, although minimizing the lift-off is preferred. Second, impedance analysers with high sample rates make high-speed inspection possible. This research assesses the damage detection capabilities of eddy current probes on CFRP samples with artificial and realistic damage. To support the aptitude of the ECT method for these needs, the CFRP material is characterized and numerical simulations are performed in order to develop optimized and tailored ECT probes for the detection of defects with different morphologies, namely fibre breakage and delaminations, and to take into consideration the highly anisotropic electrical bulk resistivity of the CFRP material. Different ECT probes were designed, produced and experimentally validated. The experiments were performed at a high inspection speed (4 m/s) and the high sensitivity of the probes was demonstrated.

This paper presents the development and the results of a customized eddy current (EC) non-destructive testing (NDT) system for highly demanding online inspection conditions. Several planar eddy current array probes were designed, numerically simulated and experimentally compared for the inspection of low conductivity unidirectional carbon fibre reinforced polymer (CFRP) ropes. The inspections were performed using a dedicated scanner device at 4 m/s with 3 mm probe lift-off where defects under 1 mm were detected with an excellent SNR. Different defect morphologies and sizes, such as broken fibres and lateral cuts, were successful detected and compared to conventional probes.

Online monitoring of carbon fiber reinforced plastic (CFRP) ropes requires non-destructive testing (NDT) methods capable of detecting multiple damage types at high inspection speeds. Three NDT methods are evaluated on artificial and realistic imperfections in order to assess their suitability for online monitoring of CFRP ropes. To support testing, the microstructure and electrical conductivity of a carbon fiber rope is characterized. The compared methods are thermography via thermoelastic stress analysis, ultrasonic testing with commercial phased array transducers, and eddy current testing, supported by tailor-made probes. While thermoelastic stress analysis and ultrasonics proved to be accurate methods for detecting damage size and the shape of defects, they were found to be unsuitable for high-speed inspection of a CFRP rope. Instead, contactless inspection using eddy currents is a promising solution for real-time online monitoring of CFRP ropes at high inspection speeds.

n/a